Оne of cellular technology approaches to skull bones plasty has been demonstrated in an experimental investigation. These bones are hardly able to recover, therefore with their extensive damage there is a necessity to use various plastic material.
ln the experiment Chinchilla rabbits were exposed. Вone marrow for stromal cells isolation was derived by a standard method. Having received the required expansion of cells in culture, they were allocated on granules of bone-plastic glass-ceramic material Biosit with the
diameter of 0.3-1.0 mm. This construction was inserted into a parietal bone modeled defect with its diameter of 1.0 cm. The results were assessed with light and electron scanning microscopy at 60 and 120 days. The cell culture has been stated to adhere granule surface and results in rapid bone defect recovery within the damaged area in combination with bone-plastic material.
В экспериментальном исследовании продемонстрирован один из подходов клеточных технологий для пластики костей мозгового черепа. Данные кости характеризуются низкой способностью к восстановлению, поэтому при их обширных повреждениях возникает необходимость использования различных пластических материалов. Эксперимент выполнен на кроликах породы Шиншилла. Костный мозг для выделения фракции стромальных клеток получали по стандартной схеме. После наращивания необходимого количества клеток в культуре их мобилизовали на гранулах костнопластического стеклокерамического материала - «Биосит» диаметром 0,3-1,0 мм. Полученную конструкцию вносили в модельный дефект теменной кости диаметром 1,0 см. Результаты оценивали при помощи световой и электронной сканирующей микроскопии на сроках 60 и 120 суток. Установлено, что культура клеток адгезируется к поверхности гранул и, будучи перенесенной в область повреждения, в сочетании с костнопластическим материалом приводит к быстрому устранению костного дефекта.